The effect of cement raw mix waste dust on porcelain tile properties

15/03/2019

Autores: Aydin, T. et Al

Nowadays, the recycling of industrial waste is one of the priority issues. Recycling studies related with reducing the negative effects of wastes on the environment are becoming increasingly important. It was believed that nothing was beyond recycling, and manufacturers should take greater responsibility for their part in the waste economy to apply cyclical solutions to an expanding breadth of new product categories. Cement raw mix contains silicate, alumina, iron oxide, and limestone. Raw mix contains SiO2, Al2O3, CaO, Fe2O3, MgO, Na2O, and K2O in higher ratio. The high presence of these oxides in the raw mix powder makes raw powder an alternative source of raw material for porcelain tile compositions. In this study, raw mix dust was used instead of sodium feldspar in a standard porcelain tile composition, at a rate of 1, 5, 10, and 15% by weight. The specimens were sintered at 1210 °C. Flexural strength, firing shrinkage, water absorption, porosity, and other technological properties were investigated. It has been determined that the body containing 1% of the raw mix powder improved its physical and mechanical properties compared to the standard body.

Si desea más información póngase en contacto con el Centro de Documentación

Comments are closed.



ITC © 2011  |  T.+34 964342424  |   F.+34 964342425  |   info@itc.uji.es  |   Av. Vicente Sos Baynat s/n, 12006, Castellón de la Plana, Spain  |   Aviso legal  |   Protección de datos  |   Accesibilidad